金屬在堿液中的應力腐蝕破裂稱堿脆。碳鋼、低合金鋼、不銹鋼等多種金屬材料皆可發生堿脆。碳鋼（含低合金鋼）發生堿脆的趨向見圖8.1.6。輸送NaOH的碳鋼或低合金鋼管道在一定的條件下，能引起碳鋼材料的應力腐蝕開裂（堿脆）。

  由(you)圖8.1.6可(ke)知，氫(qing)(qing)氧(yang)化鈉(na)濃(nong)(nong)度(du)在5％以上的(de)(de)全部濃(nong)(nong)度(du)范圍內碳(tan)鋼(gang)幾乎都可(ke)能產(chan)生堿(jian)(jian)(jian)(jian)脆，堿(jian)(jian)(jian)(jian)脆的(de)(de)最(zui)(zui)低溫(wen)度(du)為50℃，所需堿(jian)(jian)(jian)(jian)液(ye)的(de)(de)濃(nong)(nong)度(du)為40％～50％。以沸點(dian)附近的(de)(de)高(gao)(gao)溫(wen)區(qu)最(zui)(zui)易發生。裂紋(wen)呈晶間(jian)型。奧氏體(ti)不(bu)銹(xiu)(xiu)鋼(gang)發生堿(jian)(jian)(jian)(jian)脆的(de)(de)趨向見圖8.1.7。氫(qing)(qing)氧(yang)化鈉(na)濃(nong)(nong)度(du)在0.1％以上的(de)(de)濃(nong)(nong)度(du)時(shi)18-8型奧氏體(ti)不(bu)銹(xiu)(xiu)鋼(gang)即可(ke)發生堿(jian)(jian)(jian)(jian)脆。以氫(qing)(qing)氧(yang)化鈉(na)濃(nong)(nong)度(du)40％最(zui)(zui)危險，這(zhe)時(shi)發生堿(jian)(jian)(jian)(jian)脆的(de)(de)溫(wen)度(du)為115℃左右(you)。超低碳(tan)不(bu)銹(xiu)(xiu)鋼(gang)的(de)(de)堿(jian)(jian)(jian)(jian)脆裂紋(wen)為穿晶型，含碳(tan)量高(gao)(gao)時(shi)，堿(jian)(jian)(jian)(jian)脆裂紋(wen)則為晶間(jian)型或混合型。當奧氏體(ti)不(bu)銹(xiu)(xiu)鋼(gang)中加入2％鉬時(shi)，則可(ke)使其(qi)堿(jian)(jian)(jian)(jian)脆界限縮(suo)小，并向堿(jian)(jian)(jian)(jian)的(de)(de)高(gao)(gao)濃(nong)(nong)度(du)區(qu)域移動。鎳和鎳基合金具有較高(gao)(gao)的(de)(de)耐應(ying)力腐蝕的(de)(de)性能，它的(de)(de)堿(jian)(jian)(jian)(jian)脆范圍變得(de)狹窄(zhai)，而(er)且位于(yu)高(gao)(gao)溫(wen)濃(nong)(nong)堿(jian)(jian)(jian)(jian)區(qu)。

  一般情況下，當(dang)NaOH濃度和溫度超出表8.1.3的(de)規定時，應對焊(han)縫（含熱(re)影響區）進行消除應力熱(re)處(chu)理。

  表(biao)8.1.3 NaOH 濃度和(he)溫(wen)度應對焊縫（含熱影響區）進行(xing)消除應力熱處理的界限(xian)

  當NaOH濃(nong)度和溫度超出表8.1.4的規定時，應考慮采用(yong)含鎳(nie)合金(jin)。

 碳鋼(gang)和鎳合金鋼(gang)在NaOH溶液中(zhong)的應用范圍見圖(tu) 8.1.8 所示